规格 | 条件 | 度量标准 | U.S. | |
密度 | ASTM D792 | 1.01 g/cm³ | 1.01 g/cm³ | |
吸湿-24小时 | ASTM D570 | 0.48% | 0.48% | |
水分饱和 | ASTM D570 | 1.15% | 1.15% | |
机械性能 | ||||
拉伸强度(屈服) | ASTM D638 | 37 MPa | 5366 psi | |
拉伸强度(最终) | ASTM D638 | 48 MPa | 6961 psi | |
拉伸模量 | ASTM D638 | 1517 MPa | 220 ksi | |
屈服延伸率(%) | ASTM D638 | 5% | 5% | |
断裂伸长率(%) | ASTM D638 | 47% | 47% | |
挠曲强度(屈服) | ASTM D790 | 42 MPa | 6091 psi | |
挠曲强度(最终) | ASTM D790 | 46 MPa | 6672 psi | |
挠曲模量 | ASTM D790 | 1310 MPa | 190 ksi | |
邵氏硬度 D | ASTM D2240 | 74 | 74 | |
洛氏硬度 L | ASTM D785 | 69 | 69 | |
洛氏硬度 M | ASTM D785 | 34 | 34 | |
冲击强度(悬臂缺口冲击试验,23℃) | ASTM D256 | 74 J/m | 1.4 ft-lb/in | |
冲击强度(悬臂无缺口冲击试验,23℃) | ASTM D256 | 1486 J/m | 27.8 ft-lb/in | |
加德纳落锤冲击试验 | ASTM D5420 | 11.8 J | 8.7 ft-lb | |
热性能 | ||||
热挠曲温度(热变形) | ASTM D648 @ 0.45 MPa @ 1.82 MPa | 188℃ 88℃ | 370 °F 118 °F | |
热膨胀系数 | ASTM E831 @ 0 - 50℃ @ 85 - 145℃ | 120 µm/m-℃ 342 µm/m-℃ | 66.7 µin/in-°F 190 µin/in-°F | |
比热容 | ASTM E1269 | 1.75 J/g-℃ | 0.418 BTU/lb-°F | |
导热系数 | ASTM E1225 | 0.51 W/m-K | 3.5 BTU-in/hr-ft2-°F | |
易燃性 | UL 94 | HB | HB | |
电气性能 | ||||
体积电阻率 | ASTM D257 | 1.3 X 1013 ohm-cm | 1.3 X 1013 ohm-cm | |
表面电阻率 | ASTM D257 | 4.9 X 1012 ohm | 4.9 X 1012 ohm | |
消耗因数,1 KHz | ASTM D150 | 0.050 | 0.050 | |
介电常数,1 KHz | ASTM D150 | 4.5 | 4.5 | |
介电强度 | ASTM D149 | 18.5 kV/mm | 470 kV/in |